Made from chlorinated rubber, plasticizer, iron oxide red, additives, solvents, etc. It has good resistance to water, alkali, salt spray, and alternating dry and wet properties, and the paint film is tough and has good sealing performance.
Design purpose
It can be used as an additional coating for chlorinated rubber aluminum powder anti rust paint to enhance its anti-corrosion effect; It can be used as a sealing paint for repairing old ship coatings, and is also suitable for rust prevention of ships, port machinery, offshore platforms, and other steel structures.
Physical parameters
Color: Iron Red
Gloss: Matte
Theoretical coating rate: 270g/㎡, 4.93 ㎡/L (based on 70 μ M dry film meter, excluding losses)
Specific gravity: approximately 1.33
Drying time: 23 ± 2 ℃: surface dry ≤ 2h, solid dry ≤ 8h
Flash point: 38 ℃
Storage period: 12 months
Construction instructions
Mixing ratio: single can
Maturation time: Open and stir well before use
Applicable period: unlimited
Construction method: high-pressure airless spraying, air spraying, manual brushing, roller coating
Diluent: X-14 Chlorinated rubber coating diluent
|
|
High pressure airless spraying |
Aerated spraying |
Manual brushing and roller coating |
|
Maximum dilution amount |
5% |
10% |
3% |
|
orifice |
0.4-0.5mm |
2.0-2.5mm |
- |
|
Ejection pressure |
15-20MPa |
0.3-0.4MPa |
- |
Tool cleaning: X-14 chlorinated rubber coating thinner
Film thickness: Wet film: 200 μ m. Dry film: 70 μ M
Painting interval
|
Substrate temperature |
0℃ |
20℃ |
30℃ |
| shortest |
24h |
8h |
6h |
| longest |
unlimited |
||
Product Description
Made from chlorinated rubber, plasticizer, iron oxide red, additives, solvents, etc. It has good resistance to water, alkali, salt spray, and alternating dry and wet properties, and the paint film is tough and has good sealing performance.
Design purpose
It can be used as an additional coating for chlorinated rubber aluminum powder anti rust paint to enhance its anti-corrosion effect; It can be used as a sealing paint for repairing old ship coatings, and is also suitable for rust prevention of ships, port machinery, offshore platforms, and other steel structures.
Physical parameters
Color: Iron Red
Gloss: Matte
Theoretical coating rate: 270g/㎡, 4.93 ㎡/L (based on 70 μ M dry film meter, excluding losses)
Specific gravity: approximately 1.33
Drying time: 23 ± 2 ℃: surface dry ≤ 2h, solid dry ≤ 8h
Flash point: 38 ℃
Storage period: 12 months
Construction instructions
Mixing ratio: single can
Maturation time: Open and stir well before use
Applicable period: unlimited
Construction method: high-pressure airless spraying, air spraying, manual brushing, roller coating
Diluent: X-14 Chlorinated rubber coating diluent