Product Description
Composed of high chlorinated polyethylene, synthetic resin, plasticizer, pigment, additive, solvent, etc., aluminum pink is double canned, while others are single canned. This coating has excellent weather resistance, chemical atmospheric corrosion resistance, acid, alkali, salt corrosion resistance, good light and color retention of the paint film, bright and beautiful color, and good outdoor applicability.
Design purpose
Suitable for anti-corrosion decoration on the surface of outdoor steel structures and concrete facilities.
Physical parameters
Color: White, Yellow, Blue (other colors available as needed)
Gloss: Semi gloss
Theoretical coating rate:
175g/㎡, 180g/㎡, 170g/㎡ (corresponding to color)
6.70 ㎡/L, 6.70 ㎡/L, 6.60 ㎡/L (using dry film 35 μ M, excluding losses)
Specific gravity: approximately 1.17 1.20 1.18 (corresponding to color)
Drying time: 23 ± 2 ℃: surface drying ≤ 1 hour, solid drying ≤ 24 hours
Flash point: 26 ℃
Storage period: 12 months
Construction instructions
Mixing ratio: single can (aluminum pink component A: component B=8.5:1.5)
Maturation time: Open to use (aluminum pink mixed to use)
Applicable period: unlimited
Construction method: manual brushing and roller coating
Diluent: X-16 high chlorinated polyethylene coating diluent
Maximum dilution:<5%
Tool cleaning: X-16 high chlorinated polyethylene coating diluent
Film thickness: Wet film: 150 μ m. Dry film: 35 μ M
Painting interval
0 ℃: minimum 24 hours, maximum unlimited;
25 ℃: minimum 12 hours, maximum unlimited;
35 ℃: minimum 8 hours, maximum unlimited.
Surface treatment: Apply high chlorinated polyethylene enamel (outdoor type) within the specified coating time interval of the previous coating.
Construction conditions: Before construction, the coating must be thoroughly and evenly mixed.
The substrate temperature must be 3 ℃ above the dew point.
Generally, the construction temperature of high chlorinated polyethylene anti-corrosion coatings should be between 0-35 ℃. Pay attention to weather and temperature changes during construction; On rainy, foggy, snowy days, with a relative humidity greater than 85%, and during hot summer weather, construction cannot be carried out under strong direct sunlight.
Front matching coatings: C17 high chlorinated polyethylene iron red anti-corrosion primer, C171 high chlorinated polyethylene cloud iron anti-corrosion intermediate paint, C08-4 two component epoxy red lead anti-corrosion primer, C181 chlorinated rubber iron red anti-corrosion primer
Rear supporting coating: C17 high chlorinated polyethylene iron red anti-corrosion primer.
Suggested number of coats: 2-3 coats, with a dry film of 80-100 μ M.
Packaging specification: 20 kilograms in a 20 liter container. Aluminum pink component A is packaged in a 20 liter container of 17 kilograms, while component B is packaged in a 20 kilogram container.
Note: The paint film thickness can be modified according to the purpose or area of use, but this will correspondingly change the coating rate, drying time, and repainting interval.
matters needing attention
Before construction, the high chlorinated polyethylene heavy-duty anti-corrosion coating must be thoroughly mixed and evenly mixed before construction can be carried out.
High chlorinated polyethylene heavy-duty anti-corrosion coating can be applied using brush or roller coating methods. The coating should be carried out in a crisscross order and maintained at a certain speed to ensure the formation of a dense and uniform coating, reducing the occurrence of air holes. When using brush coating, the number of times to apply should not be too many, usually three times. If the number of times to apply the topcoat is too many, the bottom or intermediate coating may be rough and cause discoloration of the topcoat.
The dilution of high chlorinated polyethylene heavy-duty anti-corrosion coating should use a special diluent of high chlorinated polyethylene heavy-duty anti-corrosion coating. When applying at low temperatures and after sandblasting treatment, the coating does not need to be diluted. When constructing steel surfaces under high temperature conditions in summer, the primer must be diluted before brushing, but the dilution dosage must be controlled at 5% -10% of the coating amount.
The coating interval of high chlorinated polyethylene heavy-duty anti-corrosion coating is that after the first primer is applied to the steel surface after rust removal, the subsequent primer, intermediate paint, and topcoat should be applied within the specified coating interval.
security
Please pay attention to the safety precautions on the packaging label. In addition, safety regulations stipulated by relevant national or local governments should also be followed. Avoid long-term inhalation of solvent vapors or paint mist. Skin and eyes should not come into contact with this product. When working in narrow or non ventilated areas, strong ventilation must be provided, and protective equipment should be worn despite good ventilation conditions.
Notes
The data related to this manual was obtained in the laboratory, and may vary slightly during actual use due to changes in environmental conditions;
If there are any changes to the above data, the latest manual of our company shall prevail without prior notice.