Composed of long-oil pentaerythritol alkyd resin, mica iron oxide, aluminum powder, drying agent, solvent, etc. It has good adhesion, good moisture resistance, resistance to atmospheric erosion, and good adhesion to the bottom surface.
Design purpose
Black metal is used as an intermediate paint and anti rust paint.
Physical parameters
Color: reddish brown or grayish brown
Gloss: Matte
Theoretical coating rate: 115g/㎡, 11.74 ㎡/L (based on 40 μ M dry film meter, excluding losses)
Specific gravity: approximately 1.35
Drying time: 23 ± 2 ℃: surface drying ≤ 4 hours, solid drying ≤ 24 hours
Flash point: 35 ℃
Storage period: 12 months
Construction instructions
Mixing ratio: single can
Maturation time: Open and stir well before use
Applicable period: unlimited
Construction method: high-pressure airless spraying, air spraying, manual brushing, roller coating
Diluent: X-6 Alkyd Paint Diluent
|
|
High pressure airless spraying |
Aerated spraying |
Manual brushing and roller coating |
|
Maximum dilution amount |
5% |
10% |
3% |
|
orifice |
0.4-0.5mm |
2.0-3.0mm |
- |
|
Ejection pressure |
12-15MPa |
0.3-0.5MPa |
- |
Tool cleaning X-6 alkyd paint thinner
Paint film thickness Wet film: 60 μ m. Dry film: 40 μ M
Painting interval
|
Substrate temperature |
5℃ |
20℃ |
30℃ |
|
shortest |
48h |
24h |
12h |
|
longest |
unlimited |
||
surface treatment
Steel with oxide skin: needs to be shot blasted or sandblasted to the Swedish rust removal standard Sa2 level;
Oxygenated skin free steel: polished to Swedish rust removal standard St3 using pneumatic or electric tools;
Steel coated with workshop primer: needs to undergo secondary rust removal to meet the Swedish rust removal standard St3 level.
Construction conditions:
The substrate temperature must be 3 ℃ above the dew point, and the relative humidity must be less than 85%.
When the temperature of the construction substrate is below 5 ℃, the reaction between epoxy and curing agent stops and construction cannot proceed.
Previous supporting coatings: C08-30 two-component epoxy zinc rich workshop primer, CO8-10 two-component epoxy zinc powder workshop primer, C08-2 two-component epoxy iron red primer, C08-14 two-component inorganic zinc silicate workshop primer, C06-1 alkyd iron red antirust paint, C53-31 red lead alkyd antirust paint, etc.
Rear supporting coatings: C22-1 alkyd enamel (universal type), C22 alkyd enamel (weather resistant type), etc.
Packaging specification: 20 kilograms in an 18.5-liter container.
security
Avoid long-term inhalation of solvent vapors or paint mist, and do not come into contact with skin or eyes. When working in narrow or poorly ventilated areas, strong ventilation must be provided, and even if the ventilation conditions are good, protective equipment should be worn.
Notes
The above dry and wet film thickness refers to the indicators during high-pressure airless spraying;
The data related to this manual was obtained in the laboratory, and the actual product may differ slightly from it;
If there are any changes to the above data, the latest manual of our company shall prevail without prior notice.