This product is made of synthetic resin as the base material, with the addition of rust resistant pigments, additives, solvents, etc. This coating has the characteristics of high solid content, good adhesion to non-ferrous metal substrates, and excellent mechanical properties.
Design purpose
Special primer for anti-corrosion of non-ferrous metal surfaces such as galvanized sheet, aluminum sheet, stainless steel, etc.
Physical parameters
Color: light green
Gloss: Matte
Theoretical coating rate: 100g/㎡, 14.2 ㎡/L (based on 30 μ M dry film meter, excluding losses)
Specific gravity: approximately 1.50
Drying time: 23 ± 2 ℃: surface drying for 4 hours, solid drying for 24 hours
Complete curing: 23 ± 2 ℃: 7d
Flash point: 29 ℃ for component A, 20 ℃ for component B
Storage period: 12 months
Construction instructions
Mixing ratio: Component A (paint): Component B (curing agent)=20:3
Maturation time: 23 ± 2 ℃: 30min
Pot life: 23 ± 2 ℃: 8h
Construction method: high-pressure airless spraying, air spraying, manual brushing, roller coating
Diluent: X-7 epoxy coating diluent
|
|
High pressure airless spraying |
Aerated spraying |
Manual brushing and roller coating |
|
Maximum dilution amount |
5% |
5% |
3% |
|
orifice |
0.4-0.5mm |
2.0-2.5mm |
- |
|
Ejection pressure |
12-20MPa |
0.3-0.5MPa |
- |
Tool cleaning X-7 epoxy coating thinner
Paint film thickness Wet film: 60 μ m. Dry film: 30 μ M
Painting interval
|
Substrate temperature |
5℃ |
20℃ |
30℃ |
|
Min long |
48h |
24h |
12h |
|
Max long |
14d |
7d |
3d |
Product Description
This product is made of synthetic resin as the base material, with the addition of rust resistant pigments, additives, solvents, etc. This coating has the characteristics of high solid content, good adhesion to non-ferrous metal substrates, and excellent mechanical properties.
Design purpose
Special primer for anti-corrosion of non-ferrous metal surfaces such as galvanized sheet, aluminum sheet, stainless steel, etc.
Physical parameters
Color: light green
Gloss: Matte
Theoretical coating rate: 100g/㎡, 14.2 ㎡/L (based on 30 μ M dry film meter, excluding losses)
Specific gravity: approximately 1.50
Drying time: 23 ± 2 ℃: surface drying for 4 hours, solid drying for 24 hours
Complete curing: 23 ± 2 ℃: 7d
Flash point: 29 ℃ for component A, 20 ℃ for component B
Storage period: 12 months
Construction instructions
Mixing ratio: Component A (paint): Component B (curing agent)=20:3
Maturation time: 23 ± 2 ℃: 30min
Pot life: 23 ± 2 ℃: 8h
Construction method: high-pressure airless spraying, air spraying, manual brushing, roller coating
Diluent: X-7 epoxy coating diluent